Nickel 200/201 pipes and tubes

Nickel 200/201 Pipes & Tubes

Nickel 200/201 pipes and tubes, these ferromagnetic pipe have a low electrical resistance. Because they are low carbon alternative to this alloy, they are not as hard as some of their rivals. Their annealed stiffness is poor. Additionally, their toughening rate is really low. High-level creep resistance is provided by them. They are ductile and incredibly sturdy. At high temperatures, they show increased creep qualities. They have exceptional oxidation resistance.

ASME SB 730 Nickel 201 Tubes Exporter, DIN 2.4068 Tubing, Nickel 200, B163 Alloy 200 Tubing Supplier, UNS N02200, ASTM B751 Nickel 200 Welded Tube, ASTM B161 Nickel Alloy 201 Seamless Pipes Manufacturer in India.

Under the majority of air circumstances, the high concentration of nickel provides corrosion resistance. It is well known that these have precise dimensional requirements. They therefore have nice, eye-catching surface finishes. Companies value them even in the global market because of their dependability, sturdiness, and ease of use. In keeping with that, transportation is simple.

ASTM B725 Nickel® Alloy 200 ERW Dealer, Nickel UNS N02201, DIN 2.4066 ERW Tubing, Nickel 201 Seamless Pipe Trader, ASME SB775 Nickel 201 Welded Stockist, Nickel 201, B730 Nickel 200 Tube, ASME SB163 Nickel 200 Seamless Tubes Supplier in India.

These have the ability to combat corrosive alkalis at a range of temperatures and concentrations. Even at high temperatures, the unwavering strength of our nickel pipe is maintained. In addition, they are resistant to a variety of dangerous corrosion. This pipe can be made in any shape using hot forming techniques, as well as cold forming techniques. All of our pipe are made of nickel. Its resistance to corrosion is flawless. They have relatively low electrical resistivity is caused by the iron component in them. It can be used as conducting leads and terminals in electrical and electronic components due to its low electrical resistance.

200/201 NICKEL EQUIVALENT GRADES

STANDARD WERKSTOFF NR. UNS JIS BS GOST AFNOR EN
Nickel 200 2.4066 N02200 NW 2200 NA 11 НП-2 N-100M Ni 99.2
Nickel 201 2.4068 N02201 NW 2201 NA 12 НП-2 - LC-Ni 99

Specification of Nickel Alloy 200/201 Pipes and Tubes


Nickel Seamless Pipes and Tubes : ASTM B161, B163 / ASME SB161, SB163
Nickel Welded Pipes and Tubes : ASTM B775, B725, B751, B730 / ASTM SB775, SB725, SB751, SB730
Pipe Size : Seamless 1/2″ – 10″ , Welded 1/2″ – 48″.
Tube Size : 4 to 219mm W. T.: 0.5 to 20mm
Schedule : SSCH20, SCH30, SCH40, STD, SCH80, XS, SCH60, SCH80, SCH120, SCH140, SCH160, XXS
Type : Seamless / ERW / Welded / Fabricated Pipes
Form : Round Pipes/Tubes, Square Pipes/Tubes, Rectangular Pipe/Tubes, Coiled Tubes, “U” Shape, Pan Cake Coils, Hydraulic Tubes
Length : Single Random, Double Random & Required Length
End : Plain End, Beveled End, Treaded
End Protection : Plastic Caps
Inspection, Test Reports : Mill Test Certificates, EN 10204 3.1, Chemical Reports, Mechanical Reports, PMI Test Reports, Visual Inspection Reports, Third Party Inspection Reports, NABL Approved Lab Reports, Destructive Test Report, Non Destructive Test Reports
Packing : Packed in Wooden Boxes, Plastic Bags, Steel Strips Bundled, or as per Customers Requests
Specials : Sizes and Specifications other than above can be manufactured on request


CHEMICAL COMPOSITION OF NICKEL 200/201 SEAMLESS AND WELDED PIPES AND TUBES

Material / Purity: Alloy 200 Alloy 201
Ni 99.00 99.00
Fe .40 0.40
Mn 0.35 0.35
Si 0.35 0.35
C 0.15 0.02
S 0.01 0.01
Cu 0.25 0.25

MECHANICAL PROPERTIES OF NICKEL 200/201 PIPES AND TUBES

Nickel Alloy 200
Properties Metric Imperial
Tensile strength (annealed) 462 MPa 67000 psi
Yield strength (annealed) 148 MPa 21500 psi
Elongation at break (annealed prior to test) 45% 45%
Nickel Alloy 201
Properties Metric Imperial
Tensile strength (annealed) 403 MPa 58500 psi
Yield strength (annealed) 103 MPa 14900 psi
Elongation at break (annealed prior to test) 50% 50%

PHYSICAL PROPERTIES OF NICKEL 200/201 PIPES AND TUBES

Density 8.902gm/cc
Melting Point 1453 oC
Boiling Point 2732 oC
Thermal Conductivity 0.909 W/cm/K @ 298.2K
Electrical Resistivity 6.84 microhm-cm @ 20
Electronegativity 1.8 Paulings
Specific Heat 0.106 Cal/g/ K @ 25
Heat of Vaporization 91.0 K-Cal/gm atom at 2732 oC
Heat of Fusion 4.20 Cal/gm mole